I-Self Dry Silver Top Coat JH-9320

Incazelo emfushane:

I gama le-brand:JUNHE

Inombolo Yemodeli:JH-9320

Imininingwane Yomkhiqizo

Omaka bomkhiqizo

Imigomo Yokukhokha Nokuthumela:
Inani elincane le-oda:100 Kilogram
Inani:Kuyaxoxiswa
Imininingwane yokupakisha:I-15kg / i-Metal Barel
Isikhathi sokuthumela:Ezinsukwini eziyishumi ngemuva kokuthola inkokhelo kusengaphambili
Ikhono Lokuhlinzeka:Amathani ama-2 ngosuku

Umbala:Isiliva
PH:3.8-5.2
Ukuqina Kokunamathela(μ):I-First Coating≥15
Okungaguquguquki %:30
Ukuqina:0.7
Okumanzi Nokushisa(h):240

Incazelo

Okwethu kwe-zinc flake coating surface bulukhuni buphansi, amaphutha embotsheni kanye ne-asidi ne-alkali ukumelana, thola izifundo kubuchwepheshe befomula yasekhaya, ucwaningo lwekhwalithi ephezulu yezinto zokusetshenziswa kanye nokukhiqizwa kwe-JH-9320 zinc flake coating uketshezi olukhethekile lwe-self dry coating, kokubili kuyanda. ye-zinc flake enamathela phezu kokuqina kwendawo, ukumelana ne-asidi ne-alkali, futhi ingathuthukisa ukusebenza kwe-anticorrosion ye-coating kanye ne-zinc flake enamathelayo ehambisana nokunamathela okuhle.
Isithako esiyinhloko i-water-base inorganic silica, exutshwe nomsizi wokuvikela ukugqwala.Izindleko zomkhiqizo ziphansi.

Idatha Yezobuchwepheshe

Cha.	Into	Idatha
1	Umbala	Isiliva
2	ukujiya kwe-coating(μ)	Ukugqoka kokuqala≥15
3	okungaguquguquki %	30
4	Ukunamathela≤	2
5	Ukuvumelana nezimo(mm)≤	3
6	ubulukhuni	0.7
7	ukumelana komthelela (KG.CM)	50
8	kumanzi nokushisa(h)	240

Imiyalelo nokunaka:
1. I-Dip coating, i-spray coating njll;
2. Kufanele inyakaziswe ngokugcwele ukuze isetshenziswe;amanzi distilled noma amanzi deionized angasetshenziswa ukulungisa viscosity;Ukusebenza kwe-viscosity: 30-60s.
3. Lapho umswakama wemvelo ungaphezu kuka-85%, ungangeza utshwala obuthile bezimboni ukuze ulungise i-viscosity;
4. Isimo sokuphulukisa: 80℃/10min+140℃/30min;
5. Umshini wokuhlanza: amanzi agelezayo angasetshenziswa;
6. Gwema izinto ze-asidi, noma ukufakwa kwe-polymerization kanye nokuwohloka kuzokwenzeka;
7. Lo mkhiqizo ungasetshenziswa wodwa, indawo ehlanganisiwe icela uwoyela, ayinalo uthuli futhi yomile, kungcono ukwenza ukwelashwa kwangaphambili kokukhipha amafutha, ukuqeda amandla, kanye ne-phosphating.

Indlela yokucubungula:
I-base-coat+ 1 Ijazi eliphezulu
B 2 base-coat+ 1 Ijazi eliphezulu (ukuvikela ukugqwala okukhulu)

Ipharamitha yenqubo:
I-Dip Coating Temperature RT
I-Viscosity esebenzayo 45-60 S
I-Centrifuge 210~270 RPM/min 10s X izikhathi ezingu-4-8
(Idivayisi ye-Centrifuge ayikwazi ukuxubaniswa ne-spin dyrer)
I-Spray Coating Temperature RT
I-Viscosity esebenzayo 30~40 S
Ukwelapha: 80℃ 10min + 140℃ 20—30min
Ukuvikelwa kokugqwala kokugeleza kwenqubo ye-b
Ukumelana nokugqwala: ≥1500h (NSS)
Ukumelana namanzi olwandle: 25℃≥1500h

Idatha Yezobuchwepheshe

Cha.	Into	Idatha
1	Umbala	Isiliva
2	ukujiya kwe-coating(μ)	Ukugqoka kokuqala≥15
3	okungaguquguquki %	30
4	Ukunamathela≤	2
5	Ukuvumelana nezimo(mm)≤	3
6	ubulukhuni	0.7
7	ukumelana komthelela (KG.CM)	50
8	kumanzi nokushisa(h)	240